Product Details
Product Description :
The JiuChen Ceramic wool blanket are made from long ceramic fibres, and through double needing without binders. They exists stability and good tensile strength in 1000C-1430C. They offer superior effects in saving heat energy and refractory field.
Item Name |
HZ 1430℃ ceramic fiber blanket factory china |
Size(mm) |
Length:7200/3600 Width: 1220/610 Thickness: 20-50
(Other sizes and shapes on request. )
|
Density(kg/m3) |
96,128 |
Package |
Carton with PVC film inner OR Woven Bag with PVC film inner |
Payment |
30% T/T in advance, balance at B/L copy |
Delivery time |
7-10 days after deposit |
MOQ |
As requested |
Supply Ability |
100t per month |
Samples |
Available, please contact Ivy |
Certificates |
ISO9001-2000 |
ITEM |
PRODUCT |
COM |
STD |
HP |
HA |
HZ |
Classification Temperature(ºC) |
1100(2012℉) |
1260(2300℉) |
1260(2300℉) |
1360(2480℉) |
1430(2606℉) |
Working Temperature(ºC) |
<1000(1832℉) |
1050(1922℉) |
1100(2012℉) |
1200(2192℉) |
1350(2462℉) |
Color |
Pure White |
Pure White |
Pure White |
Pure White |
Pure White |
Density(kg/m3) |
96-128kg/m3 |
96-128kg/m3 |
96-128kg/m3 |
128-160kg/m3 |
128-160kg/m3 |
|
Line Shrinkage
(%) After 24hours
|
≤2.5
(1000℃/1832℉)
|
≤2.5
(1000℃/1832℉)
|
≤2.5
(1100℃/2012℉)
|
≤3.5
(1250℃/2282℉)
|
≤3.5
(1350℃/2462℉)
|
|
Thermal conductivity
(w/m.k)
density(128Kg/m3)
|
0.09(400℃/752F) |
0.09(400℃/752F) |
0.09(400℃/752F) |
0.132(600℃/1112F) |
0.176(600/1112F) |
|
0.176
(800ºC/1472F)
|
0.176
(800ºC/1472F)
|
0.176
(800ºC/1472F)
|
0.22
(1000ºC/1832F)
|
0.22
(1000ºC/1832F)
|
|
|
0.22
(1000 ºC/1832F)
|
0.28
(1200ºC/2192F)
|
|
Tensile strength (Mpa) |
0.04 |
0.04 |
0.04 |
0.04 |
0.04 |
|
Chemical
Composition %
|
Al2O3 |
44 |
46 |
47-49 |
52-55 |
39-40 |
Al2O3+SiO2 |
96 |
97 |
99 |
99 |
- |
Al2O3+SiO2+ZrO2 |
- |
- |
- |
- |
99 |
ZrO2 |
- |
- |
- |
- |
15-17 |
Fe2O3 |
<1.2 |
<1.0 |
0.2 |
0.2 |
0.2 |
Na2O+K2O |
≤0.5 |
≤0. 5 |
0.2 |
0.2 |
0.2 |
Size(mm) |
Specification:7200X610X25/3600x610x50,other according to customer's requirement |